Аннотация к статье на английском языке:
Using x-ray diffraction analysis and electron-probe microanalysis, we have studied TiC coatings obtained by chemical vapor deposition, where the base and subsequently the coating have undergone magnetic abrasive finishing. We have found that treating the base before the coating is deposited prevents an η phase (Co6W6C) from forming in the surface layer of coated platelets. Magnetic abrasive finishing (MAF) has been found to cause an α → β transition in the cobalt phase.
Using x-ray diffraction analysis and electron-probe microanalysis, we have studied TiC coatings obtained by chemical vapor deposition, where the base and subsequently the coating have undergone magnetic abrasive finishing. We have found that treating the base before the coating is deposited prevents an η phase (Co6W6C) from forming in the surface layer of coated platelets. Magnetic abrasive finishing (MAF) has been found to cause an α → β transition in the cobalt phase.