51. J.P. Hirth, Philos. Trans. R. Soc. London Ser., Vol 295, 1980, p 139
52. J.P. Hirth and J.R. Rise, Metall. Trans. A, Vol 11A, 1984, p 1501
53. T.Y. Zhang and J.E. Hack Metall. Mater. Trans. A, Vol 30, 1999, p 155
54. W.W. Gerberich, P. Marsh, and H. Huang, The Effect of Local Dislocation Arrangements on Hydrogen-
Induced Cleavage, Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, S.
Breummer and W.W. Gerberich, Ed., TMS-AIME, 1992, p 191–204
55. S.T. Rolfe and I.M. Barsom, Fracture and Fatigue Control in Structures, Prentice-Hall, 1977
56. R.P. Wei, S.R. Novak, and D.R. Williams, Some Important Considerations in the Development of Stress
Corrosion Cracking Test Methods, Mater. Res. Stand., Vol 12 (No. 9), Sept 1972, p 25
57. C.A. Zanis, P.W. Holsberg, and E.C. Dunn, Jr., Seawater Subcritical Cracking of HY-Steel Weldments,
Weld. J. Res. Suppl., Vol 59, Dec 1980
58. “Rapid Inexpensive Tests for Determining Fracture Toughness,” NMAB-328, National Academy of
Sciences, 1976
59. D.L. Dull and L. Raymond, Stress History Effect on Incubation Time for Stress Corrosion Crack
Growth in AISI 4340 Steel, Metall. Trans., Vol 3, Nov 1972, p 2943–2947
60. G. Liu-Nash, J.A. Todd, and S. Mostovoy, An Accelerated Test Method for Determining Near-
Threshold Stress Intensity Values in HSLA Steels, Fatigue and Fracture of Engineering Materials and
Structures, Vol 20 (No. 12), 1997, p 1657–1664
61. X.P. Zhang and Y.W. Shi, The Reasonable Design of Charpy-Size Specimen for Fracture Toughness
Test in Nuclear Surveillance, Int. J. Pressure Vessels Piping, Vol 62 (No. 3), 1995, p 219–225
62. M. Wall, C.E. Lane, and C.A. Hippsley, Fracture Criteria for Hydrogen and Temper Embrittlement in
9Cr1Mo Steel, Acta Metall. Mater., Vol 42 (No 4), April 1994, p 1295–1309
63. J.J. Lewandowski and A.W. Thompson, Hydrogen Effects on Cleavage Fracture in Fully Pearlitic
Eutectoid Steel, Hydrogen Effects on Material Behavior, TMS, 1990, p 861–870
64. R.D. Kane, M.S. Cayard, and M. Prager, “Test Procedures for Evaluation of Resistance of Steels to
Cracking in Wet H
2
S Environments,” Paper No. 519, NACE International, 1994, p 22
65. D.L. Dull and L. Raymond, Electrochemical Techniques, Hydrogen Embrittlement and Testing, STP
543, ASTM, 1974, p 20–33
66. P.J. Fast, C.S. Susskind, and L. Raymond, “Charpy V-Notched Specimens for Indexing Stress
Corrosion Cracking in HY Ship Steels and Weld Metals,” Final report, Contract F04701-78-C-0079,
The Aerospace Corporation, Aug 1979
67. P.S. Tyler, M. Levy, and L. Raymond, Investigation of the Conditions for Crack Propagation and Arrest
under Cathodic Polarization by Rising Step Load Bend Testing, Corrosion, Vol 47 (No. 2), 1991, p 82–
87
68. J.P. Fiddle, R. Bernardi, R. Broudeur, C. Roux, and M. Rapin, Disk Pressure Testing of Hydrogen
Environment Embrittlement, Hydrogen Embrittlement Testing, STP 543, ASTM, 1974, p 221–253
69. M. Beghini, G. Benamati, and L. Bertini, Hydrogen Embrittlement Characterization by Disk Pressure
Tests: Test Analysis and Application to High Chromium Martensitic Steels, J. Eng. Mater. Technol.
(Trans. ASME), Vol 118 (No. 2), 1996, p 179–185
70. Slow Strain Rate Testing for the Evaluation of Environmentally Induced Cracking: Research, STP 1210,
ASTM, 1993
71. B. Ule, F. Vodopivec, and L. Vehovar, The Application of Slow Strain Rate Tension Test for
Quantitative Evaluation of Hydrogen-Induced Cracking Susceptibility of High Strength Steels, ECF 8—
Fracture Behaviour and Design of Materials and Structures, Vol I, Engineering Materials Advisory
Services Ltd., 1990, p 461–468
72. W.W. Gerberich, Effect of Hydrogen in High-Strength and Martensitic Steels, Hydrogen in Metals,
American Society for Metals, 1976, p 115
73. B. Ule, F. Vodopivec, and L. Vehovar, The Application of Critical Strain Fracture Criteria for the
Quantitative Evaluation of Hydrogen Embrittlement of High-Strength Steels, Conference: Use of
Special Steels, Alloys and New Materials in Chemical Process Industries (Lyon, France, 22–23 May
1991), Bull. Cercle D'Etudes Met., Vol 16 (No. 1), May 1991, p 28.1–28.11
74. G. Koch, Stress Corrosion Cracking and Hydrogen Embrittlement, Fatigue and Fracture, Vol 19, ASM
Handbook, ASM International, 1996, p 481–506
75. D. Sprowls, Evaluation of Stress-Corrosion Cracking, Corrosion, Vol 13, ASM Handbook, 1987, p 245–
282
76. D. Sprowls, Evaluation of Stress Corrosion Cracking, Stress Corrosion Cracking, Materials
Performance and Evaluation, ASM International, 1992, p 363–416
77. R.H. Jones and R.E. Ricker, Stress Corrosion Cracking Mechanisms, Stress Corrosion Cracking,
Materials Performance and Evaluation, ASM International, 1992, p 1–41
78. R.W. Staehle, Understanding “Situation-Dependent Strength,” a Fundamental Objective in Assessing
the History of Stress Corrosion Cracking, EICM Proc.., R.P. Gangloff and M.B. Ives, Ed., National
Association of Corrosion Engineers, 1990, p 561
79. M.A. Gaudett and J. R. Scully, The Effects of Pre-Dissolved Hydrogen on Cleavage and Grain-
Boundary Fracture Initiation in Metastable Beta Ti-3Al-8V-4Cr-4Mo-4Zr, Met. Mater. Trans. A, Vol
30A, 1999, p 65
80. R.N. Parkins, Corros. Sci., Vol 29, 1989, p 1019
81. G. Santarini, A Morphological Model for Quantitative Characterization of Stress Corrosion Cracking,
CDI '96, T. Magnin, Ed., The Institute of Metals, p 55
82. Stress Corrosion Testing, STP 425, ASTM, 1967, p 3
83. H.L. Craig, D.O. Sprowls, and D.E. Piper, Handbook on Corrosion Testing and Evaluation, W.H. Ails,
Ed., John Wiley and Sons, 1976, p 213
84. G. Vogt, Werkstoff. Korros., Vol 29, 1978, p 721
85. N.J.H. Holroyd and G.M. Scamans, Slow-Strain Rate Stress Corrosion Testing of Aluminum Alloys,
Environment-Sensitive Fracture, STP 821, S.V. Dean, E.N. Pugh, and G.M. Ugianski, Ed., ASTM,
1984, p 202
86. R.P. Gangloff, Corrosion Fatigue Crack Propagation in Metals, EICM Proc., R.P. Gangloff and M.B.
Ives, Ed., National Association of Corrosion Engineers, 1990, p 55
87. D.J. Duquett, Corrosion Fatigue Crack Initiation Processes—A State of the Art Review, EICM Proc.,
R.P. Gangloff and M.B. Ives, Ed., National Association of Corrosion Engineers, 1990, p 45
88. R.W. Revie, Uhlig's Corrosion Handbook, 2nd ed., John Wiley & Sons, 2000
89. R. Baboian, Ed., Corrosion Tests and Standards: Application and Interpretation, ASTM, 1995
90. P.L. Andresen, Corrosion Fatigue Testing, Fatigue and Fracture, Vol 19, ASM Handbook, 1996, p 193–
209
91. J.C. Newman, Jr. and W. Elber, Ed., Mechanics of Fatigue Crack Closure, STP 982, ASTM, 1988
92. P.L. Andresen and P.G. Campbell, The Effects of Crack Closure in High Temperature Water and Its
Role in Influencing Crack Growth Data, Proc. Fourth International Symp. on Environmental
Degradation of Materials in Nuclear Power Systems—Water Reactors, National Association of
Corrosion Engineers, 1990, p 4-86 to 4-110
93. F.P. Ford, “Mechanisms of Environmental Cracking in Systems Peculiar to the Power Generation
Industry,” Final Report NP-2589, Electric Power Research Institute, 1982
94. D.J. Duquette and H.H. Uhlig, Trans. Am. Soc. Met., Vol 61, 1968, p 449
95. P.L. Andresen, R.P. Gangloff, L.F. Coffin, and F.P. Ford, Overview—Applications of Fatigue Analysis:
Energy Systems, Proc. Fatigue/87, EMACS, 1987
96. F.P. Ford, D.F. Taylor, P.L. Andresen, and R.G. Ballinger, “Corrosion Assisted Cracking of Stainless
and Low Alloy Steels in LWR Environments,” Final Report NP-5064-S, Electric Power Research
Institute, 1987
97. P.L. Andresen and F.P. Ford, Use of Fundamental Modeling of Environmental Cracking for Improved
Design and Lifetime Evaluation, J. Pressure Vessel Technol. (Trans. ASME), Vol 115 (No. 4), 1993, p
353–358
98. H.G. Nelson, Hydrogen Induced Slow Crack Growth of a Plain Carbon Pipeline Steel under Conditions
of Cyclic Loading, Effect of Hydrogen on the Behavior of Materials, A.W. Thompson and I.M.
Bernstein, Ed., The Metals Society—American Institute of Mining, Metallurgical, and Petroleum
Engineers, 1976, p 602–611
99. H.H. Johnson, Hydrogen Brittleness in Hydrogen and Hydrogen-Oxygen Gas Mixtures, Stress
Corrosion Cracking and Hydrogen Embrittlement of Iron Based Alloys, J. Hochmann, J. Slater, R.D.
McCright, and R.W. Staehle, Ed., National Association of Corrosion Engineers, 1976, p 382–389
100. P.L. Andresen and L.M. Young, Characterization of the Roles of Electrochemistry, Convection
and Crack Chemistry in Stress Corrosion Cracking, Proc. Seventh International Symposium on
Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, National
Association of Corrosion Engineers, 1995, p 579–596
101. S. Suresh and R.O. Ritchie, Int. Metals Rev., Vol 29, 1984, p 445–476
102. R. Gangloff, Corrosion Fatigue, Corrosion Tests and Standards: Application and Interpretation,
R. Baboian, Ed., ASTM, 1995
103. Electrochem. Soc., Vol 126, 1979, p 908
104. Surf. Sci., Vol 64, 1977, p 617
105. A. Carre and J. Shultz, Polymer-Aluminum Adhesion. III. Effect of a Liquid Environment, J.
Adhes., Vol 18, 1984, p 171–184
106. J.D. Venables, Review: Adhesion and Durability of Metal-Polymer Bonds, J. Mater. Sci., Vol
19, 1984, p 2431–2453
107. H. Wu, J.T. Dickinson, and S.C. Langford, Dynamic Measurements, of Humidity Attack on
Polymer/Glass Interfaces Under Stress, J. Adhes. Sci, Vol 11, 1997, p 695–717
108. S.X. Mao and A.G. Evans, The Influence of Blunting on Crack Growth at Oxide/Metal
Interfaces, Acta Mater., Vol 45, 1997, p 4263–4270
109. T.S. Oh, J. Rodel, R.M. Cannon, and R.O. Ritchie, Ceramic/Metal Interfacial Crack Growth
Toughening by Controlled Microcracks and Interfacial Geometries, Acta Metall., Vol 36, 1988, p 2083–
2093
110. S.M. Wiederhorn, S.W. Freimann, and E.R. Fuller, Jr., Effect of Water and Other Dielectrics on
Crack Growth, J. Mater. Sci., Vol 17, 1982, p 3460–3478
111. R.W. Douglas and T.M.M. El-Shamy, J. Am. Ceram. Soc., Vol 50, 1967
112. M.L. Hair, Hydroxyl Groups in Silica Surface, J. Non-Cryst. Solids, Vol 19, 1975, p 299–309
113. R.J. Charles, Glass Surface Analysis by Auger Electron Spectroscopy, J. Appl. Phys., Vol 2,
1958
114. C.G. Pantano, D.B. Dove, and G.Y. Onoda, J. Noncryst Solids, Vol 19, 1975, p 41–53
115. J.D. Venables, Review, Adhesion and Durability of Metal-Polymer Bonds, J. Mater. Sci., Vol
19, 1984, p 2431–2453
116. M.D. Thouless and R.F. Cook, Stress Corrosion Cracking in Silicon, Appl. Phys. Lett., Vol 56,
1990, p 1962–1964
117. J.I. Federer, Stress-Corrosion of SiC in an Oxidizing Atmosphere Containing NaCl, Adv. Ceram.
Mater., Vol 3, 1988, p 293–295
118. J.I. Federer, Corrosion of SiC Ceramic by Na
2
SO
4
, Adv. Ceram. Mater., Vol 3, 1988, p 56–61
119. S.G. Cook, J.A. Little, and J E. King, Corrosion of Silicon Carbide Ceramics Using
Conventional and Electrochemical Methods, Br. Corros. J., Vol 29, 1994, p 183–189
120. B.C. Burkner and T.A. Michalske, Effect of Surface Corrosion on Glass Fracture, Fracture
Mechanics of Ceramics, Vol 8, R.C. Bradt, Ed., Plenum Press, New York, 1986, p 391
121. D.P.H. Hasselman, Ultrafine Grain Ceramics, J.J. Burke, N.L. Reed, and V. Weiss, Ed.,
Syracuse University Press, 1970, p 297–315
122. M. Tomozawa and Y.-L. Peng, Surface Relaxation as a Mechanism of Static Fatigue of Pristine
Silica Glass Fibers, J. Non-Cryst. Solids, Vol 240, 1998, p 104–109
123. D.M. Marsh, Proc. R. Soc. (London) A, Vol 270, 1964
124. T.A. Michalske and S.W. Freiman, A Molecular Mechanism for Stress Corrosion in Vitreous
Silica, J. Am. Ceram. Soc., Vol 66, 1983, p 284–288
125. T.A. Michalske and B.C. Bunker, Steric Effects in Stress Corrosion Fracture of Glass, J. Am.
Ceram. Soc., Vol 70, 1987, p 780–784
126. S.W. Freiman, Effects of Chemical Environments on Slow Crack Growth in Glasses and
Ceramics, J. Geophys. Res., Vol 89, 1984, p 4072–4076
127. B.C. Bunker and T.A. Michalske, Effect of Surface Corrosion on Glass Fracture, Fracture
Mechanics of Ceramics, Vol 8, R.C. Bradt, Ed., Plenum Press, 1986, p 391
128. C.J. Simmons and S.W. Freiman, Effect of Corrosion Processes on Subcritical Crack Growth in
Glass, J. Am. Ceram. Soc., Vol 64, 1981, p 683–686
129. D.R. Clarke, B.R. Lawn, and D.H. Roach, The Role of Surface Forces in Fracture, Fracture
Mechanics of Ceramics, Vol 8, R.C. Bradt, et al., Ed., Plenum Press, 1986
130. T.A. Michalske, B.C. Bunker, and S.J. Frieman, Stress Corrosion of Ionic and Mixed
Ionic/Covalent Solids, J. Am. Ceram. Soc., Vol 69, 1986, p 721–724
131. R.F. Cook, Environmentally Controlled Nonequilibrium Crack Propagation in Ceramics, Mater.
Sci. Eng. A, Vol 260, 1999, p 29–40
132. S.M. Wiederhorn and H. Johnson, Effect of pH on Crack Propagation in Glass, J. Am. Ceram.
Soc., Vol 56, 1973, p 192–197
133. S.M. Wiederhorn, Mechanisms of Subcritical Crack Growth in Glass, Fracture Mechanics of
Ceramics, p 549–581
134. S.M. Wiederhorn and I.H. Boltz, Stress Corrosion and Static Fatigue of Glass, J. Am. Ceram.
Soc., Vol 53, 1970, p 543–548
135. B.R. Lawn, Fracture of Brittle Solids, 2nd ed., Cambridge University Press, 1993, 378 pages
136. J.R. Hellmann, J. Matsko, S.W. Freiman, and T.L. Baker, Microstructure-Mechanical Property
Relationships in 94% Alumina Ceramics, Tailoring Multiphase and Composite Ceramics, R.E. Tressler,
G.L. Messing, C.G. Pantano, and R.E. Newnham, Ed., Plenum Press, 1986, p 367–380
137. J.J. Mechlosky and S.W. Freiman, Fractographic Analysis of Delayed Failure in Ceramics,
Fractography and Materials Science, STP 733, ASTM, 1981, p 246–258
138. M. Sakai and R.C. Bradt, Fracture Toughness Testing of Brittle Materials, Int. Mater. Rev., Vol
38, 1993, p 53–79
139. S.M. Wiederhorn, Fracture Mechanics of Ceramics, Vol 2, R.C. Bradt, D.P.H. Hasselmann, and
F.F. Lange, Ed., Plenum Press, 1974, p 613–646
140. J.E. Ritter, and R.P. LaPorte, Effect of Test Environment on Stress-Corrosion Susceptibility of
Glass, J. Am. Ceram. Soc., Vol 58, 1975, p 265–267
141. S.W. Freiman, Stress-Corrosion Cracking of Glasses and Ceramics, Stress-Corrosion Cracking,
Materials Performance and Evaluation, R.H. Jones, Ed., ASM International, 1992, p 337–344
142. G.H. Michler, Correlation Between Craze Formation and Mechanical Behaviour of Amorphous
Polymers, J. Mater. Sci., Vol 25, 1990, p 2321–2334
143. A.S. Argon, Sources of Toughness in Polymers, Advances in Fracture Research, Proc. Seventh
Int. Conf. on Fracture (ICF), Vol 4, Pergamon, 1989, p 2661–2681
144. A. Carre and J. Shultz, Polymer-Aluminum Adhesion III. Effect of a Liquid Environment, J.
Adhes., Vol 15, 1983 p 151–162
145. G. Marom and D. Cohn, Deformations of Polymers and Composite under Swelling Conditions,
Plastics & Rubber: Materials & Applications, Vol 5, 1980, p 165–168
146. S.V. Hoa, Relative Influence of the Mobility and the Solubility Parameters of Fluids on the
Mechanical Behavior of High Impact Polystyrene, Polym. Eng. Sci., Vol 20, 1980, p 1157–1160
147. A.G. Atkins and Y.W. Mai, Elastic and Plastic Fracture: Metals, Polymers, Ceramics,
Composites, Biological Materials, Halsted Press, 1985, p 817
148. K.N.G. Fuller and P.G. Fox, The Temperature Rise at the Tip of Fast-Moving Cracks in Glassy
Polymers. Proc. R. Soc. (London) A, Vol 341, 1974, p 537–557
149. M.G. Wyzgoski and G.E. Novak, Stress Cracking of Nylon in Aqueous Salt Solutions. Part 3
Craze-Growth Kinetics, J. Mater. Sci., Vol 22, 1987, p 2615–2623
150. A. Moet and E. Baer, On the Mechanism of Pressure Induced Environmental Stress Cracking in
Polystyrene, J. Mater. Sci., Vol 15, 1980, p 31–41
151. M.E.R. Shanahan, M Debski, F. Bomo, and J. Shultz, J. Polym. Sci., Polymer Physics Edition,
Vol 21, 1983, p 1103–1109
152. J.G. Williams and G.P. Marshall, Environmental Crack and Craze Growth Phenomena in
Polymers, Proc. R. Soc. (London) A, Vol 342, 1975, p 55–77
153. K. Tonyali and C.E. Rogers, Stress-Cracking of Polyethylene in Organic Liquids, Polymer, Vol
28, 1987, p 1472–1477
154. M.E.R. Shanahan and J. Shultz, Environmental Stress Cracking of Polyethylene: Analysis of the
Three Zones of Behavior and Determination of Crack-Front Dimensions, J. Polym. Sci., Polymer
Physics Edition, Vol 18, 1980, p 1747–1752
155. Y.W. Mai and A.G. Atkins, On the Velocity-Dependent Fracture Toughness of Epoxy Resins, J.
Mater. Sci., Vol 10, 1975, p 2000–2003
156. J.C. Arnold, The Influence of Liquid Uptake on Environmental Stress Cracking of Glassy
Polymers, Mater. Sci. Eng. A, Vol 197, 1995, p 119–124
157. H.M. El-Hakeem and L.E. Culver, Environmental Dynamic Fatigue Crack Propagation in High
Density Polyethylene: An Empirical Modelling Approach, Int. J. Fat., Vol 3, 1981, p 3–8
158. W.-Ch.V. Wang, E.J. Kramer, and W.H. Sachse, Effects of High-Pressure CO
2
on the Glass
Transition Temperature and Mechanical Properties of Polystyrene, J. Polym. Sci., Vol 20, 1982, p
1371–1384
159. A. Peterlin and H.G. Olf, Crazing and Fracture in Crystalline, Isotactic Polypropylene and the
Effect of Morphology, Gaseous Environments, and Temperature, J. Polym. Sci., 1975, p 243–264
160. N. Brown and S. Fischer, Nucleation and Growth of Crazes in Amorphous
Polychlorotrifluoroethylene in Liquid Nitrogen, J. Polym. Sci., Polymer Physics Edition, Vol 13, 1975,
p 1979–1982
161. R.A. Duckett, B.C. Goswami, L. Stewart, I.M. Ward, and A.M. Zihlif, The Yielding and Crazing
Behaviour of Polycarbonate in Torsion under Superposed Hydrostatic Pressure, Br. Polym. J., Vol 10,
1978, p 11–16
162. K. Matsushige, S. Radcliffe, and E. Baer, The Environmental Stress-Crazing and Cracking in
Polystyrene under High Pressure, J. Macromol. Sci. Phys., Vol B11, 1975, p 565–592
163. H.Li. Pugh, Ed., High Pressure Engineering, Mechanical Engineering Publications, 1975, p 41
164. D.R. Mears, K.D. Pae, and J.A. Sauer, Effects of Hydrostatic Pressure on the Mechanical
Behavior of Polyethylene and Polypropylene, J. Appl. Phys., Vol 40, 1969, p 4229–4237
165. E.H. Andrews and L. Bevan, Mechanics and Mechanism of Environmental Crazing in a
Polymeric Glass, Polymer, Vol 13, 1972, p 337–347
166. J.R. Atkinson and P.G. Faulker, J. Appl. Polym. Sci., Vol 15, 1971, p 209
167. G.P. Marshall, G.P. Culver, and J.G. Williams, Craze Growth in Polymethylmethacrylate: A
Fracture Mechanics Approach, Proc. R. Soc. (London) A, Vol 319, 1970, p 165–187
168. M.G. Wyzgoski and G.E. Novak, Stress Cracking of Nylon Polymers in Aqueous Salt Solutions.
I. Stress-Rupture Behaviour, J. Mater. Sci., Vol 22, 1987, p 1707–1714
169. M.C. Kenney, J.F. Mandell, and F.J. McGarry, The Effects of Sea Water and Concentrated Salt
Solutions on the Fatigue of Nylon 6,6 Fibres, J. Mater. Sci., Vol 20, 1985, p 2060–2070
170. W.C. Oliver and G.M. Pharr, An Improved Technique for Determining Hardness and Elastic
Modulus Using Load and Displacement Sensing Indentation Experiments, J. Mater. Res., Vol 7, 1992, p
1564–1583
171. T.F. Page, L. Riester, and S.V. Hainsworth, The Plasticity Response of 6H-SiC and Related
Isostructural Materials to Nanoindentation, Mater. Res. Soc. Symp. Proc., Vol 522, 1998, p 113–118
172. W. Zielinski, H. Huang, S. Venkataraman, and W.W. Gerberich, Dislocation Distribution under
a Microindentation into an Iron-Silicon Single Crystal, Philos. Mag. A, Vol 72, 1995, p 1221–1237
173. D. Kramer, H. Huang, M. Kriese, J. Robach, J. Nelson, J.N.A Wright, D. Bahr, and W.W.
Gerberich, Yield Strength Predictions from the Plastic Zone around Nanocontacts, Acta Mater., Vol 47,
1998, p 333–343
174. D.S. Harding, W.C. Oliver, and G.M. Pharr, Cracking During Nanoindentation and Its Use in the
Measurement of Fracture Toughness, Thin Films: Stresses and Mechanical Properties V, Symposium,
Materials Research Society, 1995, p 663–668
175. X. Li and B. Bhushan, Micro/Nanomechanical Characterization of Ceramic Films for
Microdevices, Thin Solid Films, Vol 340, 1999, p 210–217
176. M.R. Begley, A.G. Evans, and J.W. Hutchinson, Spherical Impression of Thin Elastic Films on
Elastic-Plastic Substrates, Int. J. Solid. Struct., Vol 36, 1999, p 2773–2788
177. S.V. Hainsworth and T.F. Page, Nanoindentation Studies of the Chemomechanical Effect in
Sapphire, J. Mater. Sci., Vol 29, 1994, p 5529–5540
178. S.K. Venkataraman, D.L. Kohlstedt, and W.W. Gerberich, Continuous Microindentation of
Passivating Surfaces, J. Mater. Res., Vol 8, 1993, p 685–688
179. D.F. Bahr, J.C. Nelson, N.I. Tymiak, and W.W. Gerberich, The Mechanical Behaviour of a
Passivating Surface under Potentiostatic Control, J. Mater. Res., Vol 12, 1997, p 3345–3353
180. S.G. Corcoran, S.R. Brankovic, N. Dimitrov, and K. Sieradzki, Nanoindentation of Atomically
Modified Surfaces, Thin-Films—Stresses and Mechanical Properties VII, R.C. Cammarata, M. Nastasi,
E.P. Busso, and W.C. Oliver, Ed., Symposium Materials Research Society, 1998, p 77–84
181. M. Pang, D.E. Wilson, and D.F. Bahr, The Strength and Fracture of Passive Oxide Films on
Metals, submitted to Proc. Materials Research Society, Thin Films: Stresses and Mechanical Properties
VIII, 1999
182. Y. Katz, N.I. Tymiak, and W.W. Gerberich, Nano-mechanical Probes as New Approaches to
Hydrogen/Deformation Interaction Studies, An invited paper for Recent Advances in the Engineering
Aspects of Hydrogen Embrittlement of the Engineering Fracture Mechanics, 1999
183. N.I. Tymiak, S. Gabric-Miskulin, Y. Katz, and W.W. Gerberich, Nanoindentation Evaluation of
Hydrogen Affected Yield and Fracture in 316 Stainless Steel, Int. Conf. Environmental Degradation of
Engineering Materials, Gdansk, Poland, 1999
184. B.R. Lawn, T.P. Dabbs, and C.J. Fairbanks, Kinetics of Shear-Activated Indentation Crack
Initiation in Soda-Lime Glass, J. Mater. Sci., Vol 18, 1983, p 2785–2797
185. S. Lathabai, J. Rodel, T. Dabbs, and B.R. Lawn, Fracture Mechanics Model for Subthreshold
Indentation Flaws. I. Equilibrium Fracture, J. Mater. Sci., Vol 26, 1991, p 2157–2168
186. D. Kells and N.J. Mills, The Initiation of Indentation Fracture in Polystyrene, Philos. Mag. A,
Vol 44, 1981, p 1149–1163
187. P. Ostojic and R. McPherson, A Review of Indentation Fracture Theory: Its Development,
Principles and Limitations, Int. J. Fract., Vol 33, 1987, p 297–312
188. R.F. Cook and G.M. Pharr, Direct Observation and Analysis of Indentation Cracking in Glasses
and Ceramics, J. Am. Ceram. Soc., Vol 73, 1990, p 787–817
189. G.R. Anstis, P. Chantikul, B.R. Lawn, and D.B. Marshall, A Critical Evaluation of Indentation
Techniques for Measuring Fracture Toughness, J. Am. Ceram. Soc., Vol 64, 1981, p 533–538
190. D.B. Marshall and R.B. Lawn, Residual Stress Effect in Sharp Contact Cracking, J. Mater. Sci.,
Vol 14, 1979, p 2001–2012
191. D.B. Marshall, R.B. Lawn, and P. Chantikul, Residual Stress Effects in Sharp Contact Cracking.
Part 2. Strength Degradation, J. Mater. Sci., Vol 14, 1979, p 2225–2235
192. D.B. Marshal and A.G. Evans, Measurement of Adherence of Residually Stressed Thin Film by
Indentation. I. Mechanics of Interface Delamination, J. Appl. Phys., Vol 56, 1984, p 2632–2638
193. M. J. Matthewson, Axi-Symmetric Contact on Thin Compliant Coatings, J. Mech. Phys. Solids,
Vol 29, 1981, p 89–113
194. L.G. Rosenfeld, J.E. Ritter, T.J. Larner, and M.R. Lin, Use of the Microindentation Technique
for Determining Interfacial Fracture Energy, J. Appl. Phys., Vol 67, 1990, p 3291–3296
195. J.J. Vlassak, M.D. Drory, and W.D. Nix, A Simple Technique for Measuring the Adhesion of
Brittle Films to Ductile Substrates with Applications to Diamond-Coated Titanium, J. Mater. Res., Vol
12, 1997, p 1990–1910
196. M.D. Drory and J.W. Hutchinson, Measurement of Brittle-Film Adhesion on a Ductile Substrate
by Indentation, Proc. Roy. Soc. (London) A, 1996, p 2319–2341
197. J.W. Hoehn, S.K. Venkataraman, H. Huang, and W.W. Gerberich, Micromechanical Test
Applied to NiAl, Mater. Sci. Eng. A, Vol A192/193, 1995, p 301–308
198. P.R. Chalker, S.J. Bull, and D.S. Rickerby, A Review of the Methods for the Evaluation of
Coating-Substrate Adhesion, Mater. Sci. Eng. A, Vol A140, 1991, p 583–592
199. S.V. Hainsworth, S.J. Bull, and T.F. Page, Scratch Deformation Response of Thin CNx Coatings
at Ultra-Low Loads, Fundamentals of Nanoindentation and Nanotribology, Symposium. Materials
Research Society, 1998, p 433–438
200. T.W. Wu, Microscratch and Load Relaxation Tests for Ultra-Thin Films, J. Mater. Res., Vol 6,
1991, p 407–426
201. S. Venkataraman, D.L. Kohlstedt, and W.W. Gerberich, Continuous Microscratch Measurements
of the Practical and True Works of Adhesion for Metal/Ceramic Systems, J. Mater. Res., Vol 11, 1996,
p 3133–3145
202. D.B. Marshall and B.R. Lawn, Flaw Characteristics in Dynamic Fatigue: The Influence of
Residual Contact Stresses, J. Am. Ceram. Soc., Vol 63, 1980, p 532–536
203. J. Zhang and A.J. Ardell, Measurement of the Fracture Toughness of Ceramic Materials Using a
Miniaturized Disk-Bend Test, J. Am. Ceram. Soc., Vol 76, 1993, p 1340–1344
204. R.W. Rice, C.C Wu, and K.R. McKinney, Fracture and Fracture Toughness of Stoichiometric
MgAl
2
O
4
Crystals at Room Temperature, J. Mater. Sci., Vol 31, 1996, p 1353–1560
205. Y. Kimura, T. Yagasaki, and T. Kunio, On the Delayed Fracture Characteristics of Vickers
Indented Glass in Deionized Water, Eng. Fract. Mech., Vol 19, 1984, p 1025–1033
206. H. Matzke, Hertzian Indentation of Thorium Dioxide, ThO
2
, J. Mater. Sci., Vol 15, 1980, p 739–
746
207. P.J. Dwivedi and D.J. Green, Determination of Subcritical Crack Growth Parameters by in Situ
Observation of Indentation Cracks, J. Am. Ceram. Soc., Vol 78, 1995, p 2122–2128
208. E.R. Fuller, B.R. Lawn, and R.F. Cook, Theory of Fatigue for Brittle Flaws Originating from
Residual Stress Concentration, J. Am. Ceram. Soc., Vol 66, 1983, p 314–321
209. S.R. Choi and J.A. Salem, Slow Crack Growth of Indent Cracks in Glass with and without
Applied Stress, Mater. Sci. Eng. A, Vol A149, 1992, p 259–264
210. D.B. Marshall and B.R. Lawn, Flaw Characteristics in Dynamic Fatigue: The Influence of
Residual Contact Stresses, J. Am. Ceram. Soc., Vol 63, 1980, p 532–536
211. V.M. Sglavo and D.J. Green, The Sub-Critical Indentation Fracture Process in Soda-Lime-Silica
Glass, Eng. Fract. Mech., Vol 55, 1996, p 35–46
212. G. Binnig, H. Rohrer, C. Gerber, and E. Weibell, Tunneling Through a Controllable Vacuum
Gap, Appl. Phys. Lett., Vol 40, 1982, p 178–180
213. G. Binnig, C.F. Quate, and C. Gerber, Phys. Rev. Lett., Vol 56, 1982, p 930
214. D. Rugar and P.K. Hansma, Atomic Force Microscopy, Phys. Today, Vol 43, 1990, p 23–28
215. D. Sarid, Scanning Force Microscopy, Oxford University, 1991
216. T. Foecke, R.M. King, A.F. Dale, and W.W. Gerberich, Imaging of Cracks in Semiconductors
Using Scanning Tunneling Microscopy, J. Vac. Sci. Technol., Vol B9, 1991, p 673–676
217. T. Kinoshita, Stress Singularity Near the Crack-Tip in Silicon Carbide: Investigation by Atomic
Force Microscopy, Acta Mater., Vol 46, 1998, p 3963–3974
218. K. Jakus, S. Michael, and J.E. Ritter, Measurement of Crack Tip Inelastic Deformations Using
Digital Image Correlation, Adv. Ceram. Mater., Vol 3, 1988, p 268–272
219. S. Manne, J. Massie, V.B. Elings, P.K. Hansma, and A.A. Gewirth, Electrochemistry on a Gold
Surface Observed with the Atomic Force Microscope, J. Vac. Sci. Technol. B, Vol 9, 1991, p 950–954
220. P.K. Hansma and J. Tersoff, Scanning Tunnelling Microscopy, J. Appl. Phys., Vol 61, 1987, p
R1–23
221. P. Mrozek, Y.-E. Sung, and A. Wieckowski, Silver Deposition on the Au(111) Electrode without
Interference by Specifically Adsorbed Anions, Surf. Sci., Vol 335, 1995, p 44–51
222. S.-L. Yau, F.-R.F. Fan, and A.J. Bard, In situ STM Imaging of Silicon(111) in HF under
Potential Control, J. Electrochem. Soc., Vol 139, 1992, p 2825–2829
223. K. Komai, K. Minoshima, and M. Itoh, J. Soc. Matter. Sci. Jpn., 1994, p 336
224. K. Komai and K. Minoshima, Nanometric Visualization of Localized Damage by Scanning
Probe Microscopy, Mater. Sci. Res. Int., Vol 2, 1996, p 209–219
225. N.I. Tymiak, D.F. Bahr, J.C. Nelson, and W.W. Gerberich, “Micromechanical Probes of a
Sensitized Stainless Steel in Corrosive Environments,” Presented at TMS Fall Conference, Symposium
on Welding of Stainless Steel Alloys (Indianapolis, IN), Sept 1997